How To Weld Diamond Segments?

1. The procedure of welding segment on the blank is actually the heat-treatment process for teeth of the blank. Some of damage would occur in the blank structure. It is very important to minimize the damage.

 

2. Typically, the welding temperature ranges 600-800℃. Improper temperature would bring additional damage to the blank or segment .

 

3. Silver soldering should use high argentiferous solder, percentage over 35%. Moreover, to shorten the soldering time, it is recommended to choose low temperature and eutexia solder.

 

4. For small-size blade welding, the diameter of flange should be big, even its rim reach the bottom of slot.

 

5. For big-size blade welding, it is recommended that using cooling method to diminish the heat effects.

 

6. When utilizing fans to ventilate the working surroundings, please make sure that wind direction should be parallel with the diameter of welded blade.

 

7.To intensify the welding between blank and segment,the non - working layer on segment should be grinded according to the arc shape of blank teeth however, if there is not of non - working layer on segment, grinding the teeth of blank.

 

8. The symmetry of position and dimension should be achieved to make segment  and blank at the same plane domain .

 

9. To make welding smoothly, it is recommended to spread solver soldering paste/fluid on the interfaces of blank and segment. The purpose is to eliminate the oxide on the interfaces and facilitate the welding.

 

10. To avoid overheating, the high frequency welding should be taken at an  interval of 4-6 teeth.

 

11. It is forbidden to use flame welding.

 

12. To avoid distortion occurred on the blank, the just-welded blade should stay more than 2hrs on the welding frame before it can be taken down and suspended.

 

13. Generally, ¢1600mm blade should be suspended more than 10hrs after welded  before put into sawing. otherwise , damage would be made to the blank and lifespan of the blade would be shorten.

 

14. After welded, the blade should be cooling down unaffectedly. It is forbidden  to use water or other cooling media. Otherwise, distortion following.

 

15. To avoid distortion.